Laminating resin - 40 min mixing ratio: 100 parts resin to 40 parts hardener

• Option 1 (40023): consisting of 200 g resin + 80 g hardener
• Variant 2 (40024): consisting of 600 g resin + 240 g hardener

Description:

• Free of nonylphenol and DETA
• Low viscosity, solvent- and filler-free
• Rapid impregnation of glass, aramid, and carbon fibers
• High static and dynamic strength
• Low surface tension, good adhesion, and low shrinkage during curing
• Ideal for bonding wood, metal, Styrofoam®, etc.

Epoxy Resin L with the corresponding hardeners is the most commonly used laminating and bonding resin

Epoxy Resin L, when used with Hardener L, exhibits mechanical properties similar to those of laminating systems commonly used in aircraft construction.

Working time: 40 minutes (100 g / 20 °C)

Mixing ratio:
100 : 40 parts by weight Epoxy Resin L : Hardener L
100 : 45 parts by volume Epoxy Resin L : Hardener L

Curing time (at 23 °C): 24 hours, heat curing optional
Heat resistance: approx. 70 °C, up to a maximum of 80 °C with an additional 15 hours at 60 °C

Processing:
It can be processed using all standard methods, such as hand layup, pressure and vacuum impregnation, as well as pressing and winding.

Potential hazards - Epoxy resin L

Hazard-determining component for labeling

2,2'-[(1-methylethylidene) bis(4,1-phenyleneoxymethylene)] bisoxirane
Hexanediol diglycidyl ether
Bisphenol-F-epichlorohydrin resin

Potential Hazards - Hardener L (40 min)

Hazard-determining component for labeling

3-Aminomethyl-3,5,5-trimethylcyclohexylamine
Isophorone diamine
Benzyl alcohol
2-Piperazin-1-ylethylamine
Phenol, styrene-treated